铸造用铝合金之化学成份
|
2009-02-05 10:07:28
|
29813 浏览
|
| AC系列 |
Cu |
Si |
Mg |
Zn |
Fe |
Mn |
Ni |
Ti |
Pb |
Sn |
Cr |
AL |
| AC1A |
4.00 ~ 5.00 |
> 1.20 |
> 0.15 |
> 0.30 |
> 0.40 |
> 0.30 |
> 0.05 |
> 0.25 |
> 0.05 |
> 0.05 |
> 0.05 |
BAL |
| AC1B |
4.00 ~ 5.00 |
> 0.20 |
0.20 ~ 0.35 |
> 0.10 |
> 0.30 |
> 0.10 |
> 0.05 |
0.05 ~ 0.30 |
> 0.05 |
> 0.05 |
> 0.05 |
BAL |
| AC2A |
3.00 ~ 4.50 |
4.00 ~ 6.00 |
> 0.25 |
> 0.50 |
> 0.70 |
> 0.50 |
> 0.30 |
> 0.20 |
> 0.15 |
> 0.05 |
> 0.15 |
BAL |
| AC2B |
2.00 ~ 4.00 |
5.00 ~ 7.00 |
> 0.50 |
> 1.00 |
> 0.80 |
> 0.50 |
> 0.35 |
> 0.20 |
> 0.20 |
> 0.10 |
> 0.20 |
BAL |
| AC3A |
> 0.25 |
10.00 ~ 13.00 |
> .015 |
> 0.30 |
> 0.70 |
> 0.35 |
> 0.10 |
> 0.20 |
> 0.10 |
> 0.10 |
> 0.15 |
BAL |
| AC4A |
> 0.25 |
8.00 ~ 10.00 |
0.35 ~ .060 |
> 0.25 |
> 0.40 |
.030 ~ 0.60 |
> 0.10 |
> 0.20 |
> 0.10 |
> 0.05 |
> 0.15 |
BAL |
| AC4B |
2.00 ~ 4.00 |
7.00 ~ 10.00 |
> 0.50 |
> 1.00 |
> 0.80 |
> 0.50 |
> 0.35 |
> 0.20 |
> 0.20 |
> 0.10 |
> 0.20 |
BAL |
| AC4C |
> 0.25 |
6.50 ~ 7.50 |
.030 ~ 0.45 |
> 0.35 |
> 0.40 |
> 0.35 |
> 0.10 |
> 0.20 |
> 0.10 |
> 0.05 |
> 0.10 |
BAL |
| AC4CH |
> 0.20 |
6.50 ~ 7.50 |
0.25 ~ 0.40 |
> 0.10 |
> 0.17 |
> 0.10 |
> 0.05 |
> 0.20 |
> 0.05 |
> 0.05 |
> 0.05 |
BAL |
| AC4D |
1.00 ~ 1.50 |
4.50 ~ 5.50 |
0.45 ~ 0.60 |
> 0.30 |
> 0.50 |
> 0.50 |
> 0.20 |
> 0.20 |
> 0.10 |
> 0.05 |
> 0.15 |
BAL |
| AC5A |
3.40 ~ 4.50 |
> 0.60 |
1.30 ~ 1.80 |
> 0.15 |
> 0.70 |
> 0.35 |
1.70 ~ 2.30 |
> 0.20 |
> 0.05 |
> 0.05 |
> 0.15 |
BAL |
| AC7A |
> 0.10 |
> 0.20 |
3.60 ~ 5.50 |
> 0.15 |
> 0.25 |
> 0.60 |
> 0.05 |
> 0.20 |
> 0.05 |
> 0.05 |
> 0.15 |
BAL |
| AC7B |
> 0.10 |
> 0.20 |
9.60 ~ 11.00 |
> 0.10 |
> 0.25 |
> 0.10 |
> 0.05 |
> 0.20 |
> 0.05 |
> 0.05 |
> 0.15 |
BAL |
| AC8A |
0.80 ~ 1.30 |
11.00 ~ 13.00 |
0.80 ~ 1.30 |
> 0.15 |
> 0.70 |
> 0.15 |
0.80 ~ 1.50 |
> 0.20 |
> 0.05 |
> 0.05 |
> 0.10 |
BAL |
| AC8B |
2.00 ~ 4.00 |
8.50 ~ 10.50 |
0.60 ~ 1.50 |
> 0.50 |
> 0.80 |
> 0.50 |
0.10 ~ 1.00 |
> 0.20 |
> 0.10 |
> 0.10 |
> 0.10 |
BAL |
| AC8C |
2.00 ~ 4.00 |
8.50 ~ 10.50 |
1.60 ~ 1.50 |
> 0.50 |
> 0.80 |
> 0.50 |
> 0.50 |
> 0.20 |
> 0.10 |
> 0.10 |
> 0.10 |
BAL | |
| |
| AA系列 |
Cu |
Si |
Mg |
Zn |
Fe |
Mn |
Ti |
Sn |
Cr |
其它 |
其它 |
AL |
| X201.0 |
4.2~5.2 |
0.1 |
0.15~0.55 |
0.4 |
0.15 |
0.4 |
0.15~0.35 |
|
|
0.05g |
0.01 |
剩余 |
| 354.0 |
1.6~2.0 |
8.6~9.4 |
0.4~0.6 |
0.1 |
0.2 |
0.1 |
0.20 |
-- |
-- |
0.05 |
0.15 |
" |
| 355.0 |
1.0~1.5 |
4.5~5.5 |
0.4~0.6 |
0.3 |
0.6 |
0.5 |
0.25 |
-- |
0.25 |
0.05 |
0.15 |
" |
| C355.0 |
1.0~1.5 |
4.5~5.5 |
0.4~0.6 |
0.3 |
0.6 |
0.5 |
0.25 |
-- |
0.25 |
0.05 |
0.15 |
" |
| 356.0 |
0.25 |
6.5~7.5 |
0.2~0.4 |
0.35 |
0.6 |
0.35 |
0.25 |
-- |
-- |
0.25 |
0.05 |
" |
| A356.0 |
0.20 |
6.5~7.5 |
0.2~0.4 |
0.10 |
0.2 |
0.10 |
0.20 |
-- |
-- |
0.25 |
0.05 |
" |
| 357.0 |
0.20 |
6.5~7.5 |
0.45~0.6 |
0.05 |
0.15 |
0.03 |
0.2 |
-- |
-- |
0.05 |
0.15 |
" |
| A357.0 |
0.20 |
6.5~7.5 |
0.4~0.7 |
0.1 |
0.2 |
0.1 |
0.1~0.2 |
-- |
-- |
0.5f |
0.15 |
" |
| 359.0 |
0.20 |
8.5~9.5 |
0.5~0.7 |
0.1 |
0.2 |
0.1 |
0.2 |
-- |
-- |
0.05 |
0.15 |
" |
| A443.0 |
0.30 |
4.5~6.0 |
0.05 |
0.5 |
0.8 |
0.50 |
0.25 |
-- |
0.25 |
-- |
0.25 |
" |
| 514.0 |
0.15 |
0.35 |
3.5~4.5 |
0.15 |
0.5 |
0.35 |
0.25 |
-- |
-- |
0.05 |
0.15 |
" |
| 520.0 |
0.25 |
0.25 |
9.5~10.6 |
0.15 |
0.3 |
0.15 |
0.25 |
-- |
-- |
0.05 |
0.15 |
" |
| 535.0 |
0.05 |
0.15 |
6.2~7.5 |
-- |
0.15 |
0.10~0.25 |
0.10~0.25 |
-- |
-- |
0.05 |
0.15 |
" |
| A535.0 |
0.10 |
0.20 |
6.5~7.5 |
-- |
0.2 |
0.1~0.25 |
0.25 |
-- |
-- |
0.05 |
0.15 |
" |
| A712.0 |
0.35~0.65 |
0.15 |
0.6~0.8 |
6.0~7.0 |
0.5 |
0.05 |
0.25 |
-- |
-- |
0.05 |
0.15 |
" |
| 771.0 |
0.1 |
0.15 |
0.8~1.0 |
6.5~7.5 |
0.15 |
0.1 |
0.1~0.2 |
-- |
0.06~0.2 |
0.05 |
0.15 |
" |
| *注 |
g: Ag :0.4~1.2% | |