合金代号 |
密度ρ /g·cm-3 |
熔化温度范围 /℃ |
20～100℃时平均线膨胀系数α /μm·(m·K)-1 |
100℃时比热容с /J·(kg·K)-1 |
25℃时热导率λ /W·(m·K)-1 |
20℃时电导率κ (%IACS) |
20℃时电阻率ρ /nΩ·m |
|
ZL101 |
2.66 |
577～620 |
23.0 |
879 |
151 |
36 |
45.7 |
|
ZL101A |
2.68 |
557～613 |
21.4 |
963 |
150 |
36 |
44.2 |
|
ZL102 |
2.65 |
577～600 |
21.1 |
837 |
155 |
40 |
54.8 |
|
ZL104 |
2.65 |
569～601 |
21.7 |
753 |
147 |
37 |
46.8 |
|
ZL105 |
2.68 |
570～627 |
23.0 |
837 |
159 |
36 |
46.2 |
|
ZL106 |
2.73 |
— |
21.4 |
963 |
100.5 |
— |
— |
|
ZL108 |
2.68 |
— |
— |
— |
117.2 |
— |
— |
|
ZL109 |
2.68 |
— |
19 |
963 |
117.2 |
29 |
59.4 |
|
ZL111 |
2.69 |
— |
18.9 |
— |
— |
— |
— |
|
ZL201 |
2.78 |
547.5～650 |
19.5 |
837 |
113 |
— |
59.5 |
|
ZL201A |
2.83 |
547.5～650 |
22.6 |
833 |
105 |
— |
52.2 |
|
Zl202 |
2.91 |
— |
22.0 |
963 |
134 |
34 |
52.2 |
|
ZL203 |
2.80 |
— |
23.0 |
837 |
154 |
35 |
43.3 |
|
ZL204A |
2.81 |
544～650 |
22.03 |
— |
— |
— |
— |
|
ZL205A |
2.82 |
544～633 |
21.9 |
888 |
113 |
— |
— |
|
Zl206 |
2.90 |
542～631 |
20.6 |
— |
155 |
— |
64.5 |
|
ZL207 |
2.83 |
603～637 |
23.6 |
— |
96.3 |
— |
53 |
|
Zl208 |
2.77 |
545～642 |
22.5 |
— |
155 |
— |
46.5 |
|
ZL301 |
2.55 |
— |
24.5 |
1047 |
92.1 |
21 |
91.2 |
|
ZL303 |
2.60 |
550～650 |
20.0 |
962 |
125 |
29 |
64.3 |
|
ZL401 |
2.95 |
545～575 |
24.0 |
879 |
— |
— |
— |
|
ZL402 |
2.81 |
— |
24.7 |
963 |
138.2 |
35 |
— |